碳化鎢是一種由鎢和碳組成的化合物，化學式為WC，英文為Tungsten Carbide，也常被簡稱為Carbide（實際上carbide是碳化物的統稱）。碳化鎢的硬度極高，摩氏硬度為8.5～9，且熔點達到2870°C，電阻亦低，常被用做切削刀具材料（可切削不鏽鋼）、製造高硬度裝甲或穿甲彈彈芯，以及一些需要高硬度的運動器材零件，以及原子筆的筆尖圓珠等。
碳化鎢 
識別 CAS號 12070-12-1 性質 化學式 WC 摩爾質量 195.86 g·mol−1 g mol−1 外觀 灰黑色固體 密度 15.8 g·cm−3，固體 熔點 2870 °C, 5198 °F (3143K) 沸點 6000°C, 10832 °F (6273K) 在水中的
溶解度 不溶於水 結構 晶體結構 六方 危險性 EU分類 未列出 相關化學 品 其他陰離子 硼化鎢
氮化鎢 其他陽離子 碳化鉬
碳化鈦
碳化矽 若 非註明，所有數據都依從國際單位制，以及來自標準狀況（25 °C, 100 kPa）的條件。
Tungsten carbide, WC is an inorganic chemical compound containing equal parts of tungsten and carbon atoms. Colloquially, tungsten carbide is often simply called carbide. In its most basic form, it is a fine gray powder, but it can be pressed and formed into shapes for use in industrial machinery, tools, abrasives, as well as jewelry. Tungsten carbide is approximately three times stiffer than steel, with a Young's modulus of approximately 550 GPa,[1] and is much denser than steel or titanium. It is comparable with corundum (α-Al2O3 or sapphire) in hardness and can only be polished and finished with abrasives of superior hardness such as silicon carbide, cubic boron nitride and diamond amongst others , in the form of powder, wheels and compounds.
There are two well characterized compounds of tungsten and carbon, WC and tungsten semicarbide, W2C. Both compounds may be present in coatings and the proportions can depend on the coating method.[2]
WC can be prepared by reaction of tungsten metal and carbon at 1400–2000 °C.[3] Other methods include a patented fluid bed process that reacts either tungsten metal or blue WO3 with CO/CO2 mixture and H2 between 900 and 1200 °C.[4] Chemical vapor deposition methods that have been investigated include:[3]
- tungsten hexachloride with hydrogen, as reducing agent and methane as the source of carbon at 670 °C (1,238 °F)
WCl6 + H2 + CH4 → WC + 6 HCl
- reacting tungsten hexafluoride with hydrogen as reducing agent and methanol as source of carbon at 350 °C (662 °F)
WF6 + H2 + CH3OH → WC + 6 HF + H2O
- At high temperatures WC decomposes to tungsten and carbon and this can occur during high temperature thermal spray, e.g. high velocity oxygen fuel (HVOF) and high energy plasma (HEP) methods.[5]
- Oxidation of WC starts at 500–600 °C.[3] It is resistant to acids and is only attacked by hydrofluoric acid/nitric acid (HF/HNO3) mixtures above room temperature.[3] It reacts with fluorine gas at room temperature and chlorine above 400 °C (752 °F) and is unreactive to dry H2 up to its melting point.[3]
WC has been investigated for its potential use as a catalyst and it has been found to resemble platinum in its catalysis of the production of water from hydrogen and oxygen at room temperature, the reduction of tungsten trioxide by hydrogen in the presence of water, and the isomerisation of 2,2-dimethylpropane to 2-methylbutane.[6] It has been proposed as a replacement for the iridium catalyst in hydrazine powered satellite thrusters.[7]
Physical properties
Tungsten carbide is high melting, 2,870 °C (5,200 °F), extremely hard 8.5–9.0 Mohs scale at 22 GPa Vickers hardness (Vickers Hardness number = 2242) with low electrical resistivity (1.7–2.2×10−7 Ohm·m), comparable with metals (e.g. vanadium 1.99×10−7 Ohm·m).[3][8]
WC is readily wetted by both molten nickel and cobalt.[9] Investigation of the phase diagram of the W-C-Co system shows that WC and Co form a pseudo binary eutectic. The phase diagram also shows that there are so-called η-carbides with composition (W,Co)6C that can be formed and the fact that these phases are brittle is the reason why control of the carbon content in WC-Co hard metals is important.[9]
Structure
WC structure, carbon atoms are gray
There are two forms of WC, a hexagonal form, α-WC,[10] and a cubic high temperature form, β-WC, which has the rock salt structure.[11] The hexagonal form can be visualized as made up of hexagonally close packed layers of metal atoms with layers lying directly over one another, with carbon atoms filling half the interstices giving both tungsten and carbon a regular trigonal prismatic, 6 coordination.[10] From the unit cell dimensions[12] the following bond lengths can be determined; the distance between the tungsten atoms in a hexagonally packed layer is 291 pm, the shortest distance between tungsten atoms in adjoining layers is 284 pm, and the tungsten carbon bond length is 220 pm. The tungsten-carbon bond length is therefore comparable to the single bond in W(CH3)6 (218 pm) in which there is strongly distorted trigonal prismatic coordination of tungsten.[13]
Molecular WC has been investigated and this gas phase species has a bond length of 171 pm for 184W12C.
Machine tools
See also: Cemented carbide
Carbide cutting surfaces are often used for machining through materials such as carbon or stainless steel, as well as in situations where other tools would wear away, such as high-quantity production runs. Carbide generally produces a better finish on the part, and allows faster machining. Carbide tools can also withstand higher temperatures than standard high speed steel tools. The material is usually called cemented carbide, hardmetal or tungsten-carbide cobalt: it is a metal matrix composite where tungsten carbide particles are the aggregate and metallic cobalt serves as the matrix.
Military
Tungsten carbide is often used in armor-piercing ammunition, especially where depleted uranium is not available or is politically unacceptable. The first use of W2C projectiles occurred in German Luftwaffe tank-hunter squadrons, which used 37 mm autocannon equipped Junkers Ju 87G dive bomber aircraft to destroy Soviet T-34 tanks in World War II. Owing to the limited German reserves of tungsten, W2C material was reserved for making machine tools and small numbers of projectiles for the most elite combat pilots, like Hans-Ulrich Rudel. It is an effective penetrator due to its high hardness value combined with a very high density.
Tungsten carbide ammunition can be of the sabot type (a large arrow surrounded by a discarding push cylinder) or a subcaliber ammunition, where copper or other relatively soft material is used to encase the hard penetrating core, the two parts being separated only on impact. The latter is more common in small-caliber arms, while sabots are usually reserved for artillery use.
Tungsten carbide is also an effective neutron reflector and as such was used during early investigations into nuclear chain reactions, particularly for weapons. A criticality accident occurred at Los Alamos National Laboratory on 21 August 1945 when Harry K. Daghlian, Jr. accidentally dropped a tungsten carbide brick onto a plutonium sphere, causing the subcritical mass to go supercritical with the reflected neutrons.
Sports
Hard carbides, especially tungsten carbide, are used by athletes, generally on poles which impact hard surfaces. Trekking poles, used by many hikers for balance and to reduce pressure on leg joints, generally use carbide tips in order to gain traction when placed on hard surfaces (like rock); such carbide tips last much longer than other types of tips.
While ski pole tips are generally not made of carbide, since they do not need to be especially hard even to break through layers of ice, rollerski tips usually are. Roller skiing emulates cross country skiing and is used by many skiers to train during warm weather months.
Sharpened carbide tipped spikes (known as studs) can be inserted into the drive tracks of snowmobiles. These studs enhance traction on icy surfaces. Longer v-shaped segments fit into grooved rods called wear rods under each snowmobile ski. The relatively sharp carbide edges enhance steering on harder icy surfaces. The carbide tips and segments reduce wear encountered when the snowmobile must cross roads and other abrasive surfaces.
Some tire manufacturers, such as Nokian and Schwalbe, offer bicycle tires with tungsten carbide studs for better traction on ice. These are generally preferred over steel studs because of their wear resistance.
Domestic
Tungsten carbide is sometimes used as the rotating ball in the tips of ballpoint pens to disperse ink during writing.[15]
Tungsten carbide can now be found in the inventory of some jewelers, most notably as the primary material in men's wedding rings. When used in this application the bands appear with a lustrous dark hue often buffed to a mirror finish. The color is more similar to that of hematite than to that of platinum. The finish is highly resistant to scratches and scuffs, holding its mirror-like shine for years. Although it is possible to inlay precious metals, woods, and other materials, these are less scratch-resistant than tungsten carbide.
A common misconception held concerning tungsten carbide rings is they cannot be removed in the course of emergency medical treatment, requiring the finger to be removed instead. Emergency rooms and many full-service jewelry repair shops are equipped with jewelers' saws that can cut through tungsten carbide rings [16] without injuring the hand or finger. An easier way to remove tungsten carbide rings is to use a tool such as vice grip style locking pliers, which can be used to shatter the ring. [17]
Many manufacturers of this emerging jewelry material state that the use of a cobalt binder may cause unwanted reactions between the cobalt and the natural oils on human skin. Skin oils cause the cobalt to leach from the material. This is said to cause possible irritation of the skin and permanent staining of the jewelry itself. Many manufacturers now advertise that their jewelry is "cobalt free". This is achieved by replacing the cobalt with nickel as a binder.