From Wikipedia, the free encyclopedia

74 tantalum ← tungsten → rhenium Mo ↑ W ↓ Sg Periodic Table - Extended Periodic Table
General
Name, Symbol, Number	tungsten, W, 74
Chemical series	transition metals
Group, Period, Block	6, 6, d
Appearance	grayish white, lustrous
Standard atomic weight	183.84(1)  g·mol−1
Electron configuration	[Xe] 4f14 5d4 6s2
Electrons per shell	2, 8, 18, 32, 12, 2
Physical properties
Phase	solid
Density (near r.t.)	19.25  g·cm−3
Liquid density at m.p.	17.6  g·cm−3
Melting point	3695 K (3422 °C, 6192 °F)
Boiling point	5828 K (5555 °C, 10031 °F)
Heat of fusion	52.31  kJ·mol−1
Heat of vaporization	806.7  kJ·mol−1
Heat capacity	(25 °C) 24.27  J·mol−1·K−1
Vapor pressure P(Pa) 1 10 100 1 k 10 k 100 k at T(K) 3477 3773 4137 4579 5127 5823
Atomic properties
Crystal structure	cubic body centered
Oxidation states	6, 5, 4, 3, 2, 1, 0, −1 (mildly acidic oxide)
Electronegativity	2.36 (Pauling scale)
Ionization energies	1st: 770 kJ/mol
	2nd: 1700 kJ/mol
Atomic radius	135  pm
Atomic radius (calc.)	193  pm
Covalent radius	146  pm
Miscellaneous
Magnetic ordering	no data
Electrical resistivity	(20 °C) 52.8 n Ω·m
Thermal conductivity	(300 K) 173  W·m−1·K−1
Thermal expansion	(25 °C) 4.5  µm·m−1·K−1
Speed of sound (thin rod)	(r.t.) (annealed) 4620  m·s−1
Young's modulus	411  GPa
Shear modulus	161  GPa
Bulk modulus	310  GPa
Poisson ratio	0.28
Mohs hardness	7.5
Vickers hardness	400  MPa
Brinell hardness	380  MPa
CAS registry number	7440-33-7
Selected isotopes
Main article: Isotopes of tungsten iso NA half-life DM DE (MeV) DP 180W 0.12% 1.8×1018 y α 2.516 176Hf 181W syn 121.2 d ε 0.188 181Ta 182W 26.50% W is stable with 108 neutrons 183W 14.31% W is stable with 109 neutrons 184W 30.64% W is stable with 110 neutrons 185W syn 75.1 d β- 0.433 185Re 186W 28.43% W is stable with 112 neutrons
References

Tungsten (IPA: /ˈtʊŋstən/), also called wolfram (IPA: /ˈwʊlfrəm, -am/), is a chemical element that has the symbol W (New Latin: wolframium) and atomic number 74. A very hard, heavy, steel-gray to white transition metal, tungsten is found in several ores including wolframite and scheelite and is remarkable for its robust physical properties, especially the fact that it has the highest melting point of all the non-alloyed metals and the second highest of all the elements after carbon. The pure form is used mainly in electrical applications but its many compounds and alloys are widely used in many applications (most notably in light bulb filaments, in most X-ray tubes (as both the filament and target), and in superalloys). Tungsten is the only metal from the third transition series that is known to occur in biomolecules.

[edit] Notable characteristics

Pure tungsten is steel-gray to tin-white and is a hard metal. Tungsten can be cut with a hacksaw when it is very pure (it is brittle and hard to work when impure) and is otherwise worked by forging, drawing, extruding, or sintering. This element has the highest melting point (3422 °C) (6192 °F), lowest vapor pressure and the highest tensile strength at temperatures above 1650 °C (3000 °F) of all metals. Tungsten has the lowest coefficient of thermal expansion of any metal. Its corrosion resistance is excellent and it can be attacked only slightly by most mineral acids. Tungsten metal forms a protective oxide when exposed to air but can be oxidized at high temperature. Steel alloyed with small quantities of tungsten greatly increases its toughness.

[edit] Applications

Tungsten is a metal with a wide range of uses, the largest of which is as tungsten carbide (W₂C, WC) in cemented carbides. Cemented carbides (also called hardmetals) are wear-resistant materials used by the metalworking, mining, petroleum and construction industries. Tungsten is widely used in light bulb and vacuum tube filaments, as well as electrodes, because it can be drawn into very thin metal wires that have a high melting point. Other uses:

• A high melting point also makes tungsten suitable for space-oriented and high temperature uses which include electrical, heating, and welding applications, notably in the GTAW process (also called TIG welding).
• Hardness and density properties make this metal ideal for making heavy metal alloys that are used in armaments, heat sinks, and high-density applications, such as weights, counterweights, ballast keels for yachts and tail ballast for commercial aircraft.
• The high density makes it an ideal ingredient for darts, normally 80% and sometimes up to 97%. This allows darts containing tungsten to have a smaller diameter than those of other metals at the same weight, permitting tighter groupings.
• High speed steel contains tungsten and some tungsten steels contain as much as 18% tungsten.
• Superalloys containing tungsten are used in turbine blades and wear-resistant parts and coatings. Examples are Hastelloy and Stellite.
• Tungsten powder is used as a filler material in thermoplastic composites which are used as a nontoxic substitute for lead, in bullets, shot, and radiation shields.
• Tungsten chemical compounds are used in catalysts, inorganic pigments, and tungsten disulfide high-temperature lubricants which are stable to 500 °C (930 °F).
• Since this element's thermal expansion is similar to borosilicate glass, it is used for making glass-to-metal seals.
• It is used in kinetic energy penetrators, usually alloyed with nickel and iron or cobalt to form tungsten heavy alloys, as an alternative to depleted uranium.
• Tungsten is used as an interconnect material in integrated circuits. Contact holes are etched in silicon dioxide dielectric material, filled with tungsten and polished to form connections to transistors. Typical contact holes can be as small as 65 nm.
• Tungsten carbide is one of the hardest carbides and is used in, among other things, machine tools such as milling cutters. Tungsten carbide is the most common material used to make milling and turning tools, and used together with cobalt and carbon is often the best choice for such applications.
• Used extensively for shielding in the radiopharmaceutical industry. It is often employed when transporting individual FDG doses (called 'pigs') - the high energy of fluorine-18 makes lead much less effective.
• Tungsten is used in the emitters of focused ion beam and electron microscopes.
• Tungsten is also beginning to see uses in jewelry. Its hardness makes it ideal for rings that will never scratch, and will in turn not need polishing (this is especially good for brushed designs).

Miscellaneous: Oxides are used in ceramic glazes and calcium/magnesium tungstates are used widely in fluorescent lighting. Crystal tungstates are used as scintillation detectors in nuclear physics and nuclear medicine. The metal is also used in X-ray targets and heating elements for electrical furnaces. Salts that contain tungsten are used in the chemical and tanning industries. Tungsten 'bronzes' (so-called due to the colour of the tungsten oxides) along with other compounds are used in paints. Tungsten carbide has recently been used in the fashioning of jewelry due to its hypoallergenic nature and the fact that due to its extreme hardness it is not apt to lose its luster like other polished metals. Some types of strings for musical instruments are wound with tungsten wire.

Closeup of a tungsten filament inside a halogen lamp.

[edit] History

Tungsten (Swedish tung sten meaning "heavy stone"), even though the current name for the element in Swedish is wolfram (sometimes spelled in Swedish as volfram), from the denomination volf rahm by Wallerius in 1747, translated from the description by Agricola in 1546 as Lupi spuma, meaning "wolf's froth" after the way tin is eaten up like a wolf after sheep in the process of its extraction^[1].

It was first hypothesized to exist by Peter Woulfe in 1779 who examined wolframite and concluded that it must contain a new substance. In 1781 Carl Wilhelm Scheele ascertained that a new acid could be made from tungstenite. Scheele and Torbern Bergman suggested that it could be possible to obtain a new metal by reducing tungstic acid. In 1783 José and Fausto Elhuyar found an acid in wolframite that was identical to tungstic acid. In Spain later that year the brothers succeeded in isolating tungsten through reduction of this acid with charcoal. They are credited with the discovery of the element.

In World War II, tungsten played an enormous role in background political dealings. Portugal, as the main European source of the element, was put under pressure from both sides, because of its sources of wolframite ore. The resistance to high temperatures, as well as the extreme strength of its alloys, made the metal into a very important raw material for the weaponry industry.

[edit] Biological role

Enzymes called oxidoreductases use tungsten in a way that is similar to molybdenum by using it in a tungsten-pterin complex.

On August 20, 2002, officials representing the U.S.-based Centers for Disease Control and Prevention announced that urine tests on leukemia patient families and control group families in the Fallon, Nevada area had shown elevated levels of the metal tungsten in the bodies of both groups.[2] Sixteen recent cases of cancer in children were discovered in the Fallon area which has now been identified as a cancer cluster, (it should be noted, however, that the majority of the cancer victims are not long time residents of Fallon). Dr. Carol H. Rubin, a branch chief at the CDC, said data demonstrating a link between tungsten and leukemia is not available at present.[3]

[edit] Production trends

The neutrality or factuality of this article or section may be compromised by weasel words. You can help Wikipedia by improving these statements.

Tungsten output in 2005

Tungsten is found in the minerals wolframite (iron-manganese tungstate, FeWO₄/MnWO₄), scheelite (calcium tungstate, CaWO₄), ferberite and hübnerite. There are important deposits of these minerals in China (with about 80% world share), Russia, Austria and Portugal, reports the British Geological Survey. The metal is commercially produced by reducing tungsten oxide with hydrogen or carbon.

World tungsten reserves have been estimated at 7 million t W. Unfortunately, most of these reserves are not economically workable so far. At our current annual consumption rate, these reserves will only last for about 140 years. According to further estimates, it has been suggested that 30% of the reserves are Wolframite and 70% are Scheelite ores. Another factor that controls the tungsten supply is scrap recycling of tungsten and it has been proven to be a very valuable raw material in comparison to ore.

[edit] Compounds

The most common formal oxidation state of tungsten is +6, but it exhibits all oxidation states from -1 to +6. ^[1] Tungsten typically combines with oxygen to form the yellow tungstic oxide, WO₃, which dissolves in aqueous alkaline solutions to form tungstate ions, WO₄²⁻.

[edit] Aqueous polyoxoanions

Aqueous tungstate solutions are noted for the formation of polyoxoanions under neutral and acidic conditions. As tungstate is progressively treated with acid, it first yields the soluble, metastable "paratungstate A" anion, W₇O₂₄⁶⁻, which over hours or days converts to the less soluble "paratungstate B" anion, H₂W₁₂O₄₂¹⁰⁻. Further acidification produces the very soluble metatungstate anion, H₂W₁₂O₄₀⁶⁻, after equilibrium is reached. The metatungstate ion exists as a symmetric cluster of twelve tungsten-oxygen octahedra known as the "Keggin" anion. Many other polyoxoanions exist as metastable species. The inclusion of a different atom such as phosphorus in place of the two central hydrogens in metatungstate produces a wide variety of the so-called heteropolyanions.

See also tungsten compounds.

[edit] Isotopes

Naturally occurring tungsten consists of five isotopes whose half-lives are so long that they can be considered stable. All can decay into isotopes of element 72 (hafnium) by alpha emission; ¹⁸⁰W has been observed to have a half life of 1.8 +- 0.2 Ea. The other naturally occurring isotopes have not been observed to decay, constraining their half-lives to be: ¹⁸²W, T_1/2 > 8.3 Ea; ¹⁸⁴W, T_1/2 > 29 Ea; ¹⁸⁵W, T_1/2 > 13 Ea; ¹⁸⁶W, T_1/2 > 27 Ea. ^[2] On average, two alpha decays of ¹⁸⁰W occur in one gram of natural tungsten per year.

27 artificial radioisotopes of tungsten have been characterized, the most stable of which are ¹⁸¹W with a half-life of 121.2 days, ¹⁸⁵W with a half-life of 75.1 days, ¹⁸⁸W with a half-life of 69.4 days and ¹⁷⁸W with a half-life of 21.6 days. All of the remaining radioactive isotopes have half-lives of less than 24 hours, and most of these have half-lives that are less than 8 minutes. Tungsten also has 4 meta states, the most stable being ^179mW (t_½ 6.4 minutes).

[edit] References

• Los Alamos National Laboratory - Tungsten
• DC/AC Circuits and Electronics: Principles & Applications by Robert K. Herrick, Published by Delmar Learning 2003 for Purdue University

1. ^ Emsley, John (2000). The Elements, 3rd edition.
2. ^ National Nuclear Data Center table of nuclides,

[edit] See also

• Field emission gun
• Oliver Sacks "Uncle Tungsten: Memories of a Chemical Boyhood"

BW Bewise Inc. Willy Chen willy@tool-tool.com bw@tool-tool.com www.tool-tool.com skype:willy_chen_bw mobile:0937-618-190 Head &Administration Office No.13,Shiang Shang 2nd St., West Chiu Taichung,Taiwan 40356 TEL:+886 4 24710048 / FAX:+886 4 2471 4839 N.Branch 5F,No.460,Fu Shin North Rd.,Taipei,Taiwan S.Branch No.24,Sec.1,Chia Pu East Rd.,Taipao City,Chiayi Hsien,Taiwan

Welcome to BW tool world! We are an experienced tool maker specialized in cutting tools. We focus on what you need and endeavor to research the best cutter to satisfy users’ demand. Our customers involve wide range of industries, like mold & die, aerospace, electronic, machinery, ,,,etc. We are professional expert in cutting field. We would like to solve every problem from you. Please feel free to contact us, it’s our pleasure to serve for you. BW product including: utting tool、aerospace tool .HSS Cutting tool、Carbide end mills、Carbide cutting tool、NAS Cutting tool、Carbide end mill、Aerospace cutting tool、Carbide drill、High speed steel、Milling cutter、Core drill、Taperd end mills、Metric end mills、Miniature end mills、Pilot reamer、Electronics cutter、Step drill、Metal cutting saw、Double margin drill、Gun barrel、Angle milling cutter、Carbide burrs、Carbide tipped cutter、Chamfering tool、IC card engraving cutter、Side cutter、NAS tool、DIN tool、Special tool、Metal slitting saws、Shell end mills、Side and face milling cutters、Side chip clearance saws、Long end mills、Stub roughing end mills、Dovetail milling cutters、Carbide slot drills、Carbide torus cutters、Angeled carbide end mills、Carbide torus cutters、Carbide ball-noseed slot drills、Mould cutter、Tool manufacturer.